Ugavi wa Kiwanda cha Alumina Oksidi Poda kwa ajili ya Mipako
Jifunze Zaidi- Hali ya Bidhaa:Poda Nyeupe
- Vipimo:0.7 um-2.0 um
- Ugumu:2100kg/mm2
- Uzito wa Masi:102
- Sehemu ya Kuyeyuka:2010℃-2050 ℃
- Sehemu ya Kuchemka:2980℃
- Maji Yanayoyeyuka:Haimumunyiki Katika Maji
- Uzito:3.0-3.2g/cm3
- Maudhui:99.7%
-
Mtengenezaji wa Oksidi Nyeupe Iliyounganishwa ya Alumini Yenye Usafi wa Juu
Jifunze Zaidi- AlO3:99.5%
- TiO2:0.0995%
- SiO2 (sio bure):0.05%
- Fe2:0.08%
- MgO:0.02%
- Alkali (Soda na Potashi):0.30%
- Umbo la Fuwele:Darasa la Rhombohedral
- Asili ya Kemikali:Amphoteriki
- Mvuto Maalum:gramu 3.95/cc
- Uzito wa Wingi:Pauni 116/futi 3
- Ugumu:KNOPPS = 2000, MOHS = 9
- Sehemu ya Kuyeyuka:2,000°C
-
Alumini Nyeupe Iliyounganishwa Kusaga Kung'arisha Mchanga Ulipuaji wa Kiwango cha Juu Kinachong'aa
Jifunze Zaidi- AlO3:99.5%
- TiO2:0.0995%
- SiO2 (sio bure):0.05%
- Fe2:0.08%
- MgO:0.02%
- Alkali (Soda na Potashi):0.30%
- Umbo la Fuwele:Darasa la Rhombohedral
- Asili ya Kemikali:Amphoteriki
- Mvuto Maalum:gramu 3.95/cc
- Uzito wa Wingi:Pauni 116/futi 3
- Ugumu:KNOPPS = 2000, MOHS = 9
- Sehemu ya Kuyeyuka:2,000°C
-
F12-F220 Nyeupe Iliyochanganywa na Oksidi ya Alumina
Jifunze Zaidi- Al2O3:99.5%
- TiO2:0.0995%
- SiO2:0.05%
- Fe2:0.08%
- MgO:0.02%
- Mvuto Maalum:gramu 3.95/cc
- Ugumu:Moh 9
- Sehemu ya Kuyeyuka:2,000°C
-
Shanga za Kioo Zilizokolea
Jifunze Zaidi- Ugumu wa Moh:6-7
- Mvuto Maalum:2.5g/cm3
- Uzito wa Wingi:1.5g/cm3
- Ugumu wa Rockwell:46HRC
- Kiwango cha Mzunguko:≥80%
- Vipimo:0.8mm-7mm, 20#-325#
- Nambari ya Mfano:Shanga za Kioo Zilizokolea
- Nyenzo:Kioo cha Chokaa cha Soda
-
Mchanga wa Alumina Nyeupe Iliyochanganywa kwa Usafi wa Juu
Jifunze Zaidi- AlO3:99.5%
- TiO2:0.0995%
- SiO2 (sio bure):0.05%
- Fe2:0.08%
- MgO:0.02%
- Alkali (Soda na Potashi):0.30%
- Umbo la Fuwele:Darasa la Rhombohedral
- Asili ya Kemikali:Amphoteriki
- Mvuto Maalum:gramu 3.95/cc
- Uzito wa Wingi:Pauni 116/futi 3
- Ugumu:KNOPPS = 2000, MOHS = 9
- Sehemu ya Kuyeyuka:2,000°C